Guys, even if everything in this paper is true, the material as it is might have limited applications.
From what they show, the critical field and critical current seem very low. 2500 Oe is like 0.25 Tesla. Even REBCO at 77K is >1T. And 2500 Oe is not even at critical temperature but much lower. From skimming through the article I couldn't find the sample size of the current measurement to get the critical current density, not just current which is meaningless (and around 300 mA).
This means you can't actually push big current through this thing (yet). You can't make a powerful magnet, and you can't make viable power lines, both applications that were the hallmark of "room temperature superconductor revolution".
Of course, maybe one or a few more tweak(s) of the material and boom, it will give high J_c and B_c. I really hope it does, it would be super cool!
From what they show, the critical field and critical current seem very low. 2500 Oe is like 0.25 Tesla. Even REBCO at 77K is >1T. And 2500 Oe is not even at critical temperature but much lower. From skimming through the article I couldn't find the sample size of the current measurement to get the critical current density, not just current which is meaningless (and around 300 mA).
This means you can't actually push big current through this thing (yet). You can't make a powerful magnet, and you can't make viable power lines, both applications that were the hallmark of "room temperature superconductor revolution".
Of course, maybe one or a few more tweak(s) of the material and boom, it will give high J_c and B_c. I really hope it does, it would be super cool!