Diamond Thermal Conductivity: A New Era in Chip Cooling(spectrum.ieee.org)
spectrum.ieee.org
Diamond Thermal Conductivity: A New Era in Chip Cooling
https://spectrum.ieee.org/diamond-thermal-conductivity
46 comments
Have diamonds found their way into other industrial cooling solutions? With the research into gem grade diamonds, I have been expecting cheap ugly synthetic diamonds to be used in more products. I have long joked that I want a diamond frying pan.
3D printer nozzles, which is sort of the opposite (industrial heating products).
Part of the argument is that better heat conduction means that you can run the nozzle cooler resulting in less heat conduction to the cold side (above where you want the filament to melt) so I guess its "cooling" in a sense too.
Part of the argument is that better heat conduction means that you can run the nozzle cooler resulting in less heat conduction to the cold side (above where you want the filament to melt) so I guess its "cooling" in a sense too.
> ugly synthetic diamonds
Not any more, their quality has increased recently. Not that I care, wife and I did without them during our engagement.
Not any more, their quality has increased recently. Not that I care, wife and I did without them during our engagement.
I think the point was not that gem-grade synthetic diamonds are ugly, but that, as industry masters gem-grade production, presumably below-gem-grade production (“ugly synthetic diamonds”) would become cheap enough to deploy in more engineering settings where diamond’s other unique properties were the key concern.
I’m surprised nobody has done a phone screen yet
Large single crystal diamond, what is required for a nice transparent screen, is still quite expensive. This article is about polycrystalline diamond, which is not really that transparent, but is nearly as good at thermal conduction as monocrystalline diamond.
Your comment reminds me of apple's attempt to make sapphire screens. That didn't turn out so well.
https://www.theguardian.com/technology/2014/feb/10/sapphire-...
https://www.theguardian.com/technology/2014/feb/10/sapphire-...
Apple still uses sapphire screens on the nicer watches.
I have a Garmin with a sapphire screen. I've worn it every day for over 5 years, working on cars, in the garden, snorkelling on coral reefs.
In short, I my watch has NOT had an easy life. I've made no attempt to protect it or taken it off for anything except charging. There is barely a mark on the screen. A sapphire screen will be a hard requirement for my next watch.
In short, I my watch has NOT had an easy life. I've made no attempt to protect it or taken it off for anything except charging. There is barely a mark on the screen. A sapphire screen will be a hard requirement for my next watch.
I wear mine while rock climbing. The watch has been put through a lot of beating against all kinds of rock. I've already chewed through 3 straps on this watch. The titanium case is lightly scratched, but the screen is absolutely pristine!
This is my second sapphire Garmin, and it's absolutely worth the premium.
This is my second sapphire Garmin, and it's absolutely worth the premium.
> I've already chewed through 3 straps on this watch.
Ever consider carrying a protein bar or two?
Ever consider carrying a protein bar or two?
Even if that were cheap I don't think diamond would excel in this use case. It's of course extremely hard but I'd expect that it would be extremely prone to cracking. In addition the high index of refraction would make the diamond screen very reflective and you would need some fancy coating which of course wouldn't be as strong as diamond.
I don't know why you expect it would be prone to cracking, but it isn't - or else a wedding ring would have a life expectancy shorter than the average marriage.
As for a reflective screen, the term for that is "shiny", and could be marketed as desirable - it signals that the owner has an expensive watch. It wouldn't interfere with use, unless the user was wearing a bright headlamp.
As for a reflective screen, the term for that is "shiny", and could be marketed as desirable - it signals that the owner has an expensive watch. It wouldn't interfere with use, unless the user was wearing a bright headlamp.
> I have long joked that I want a diamond frying pan
As long as you don’t use it on a gas stove, you should be fine.
As long as you don’t use it on a gas stove, you should be fine.
Why? Diamond has very low thermal expansion, so no risk of stress/embrittlement/cracks from uneven heating.
Or you mean it'll catch fire? Also not a concern. That is supposed to happen at a temperature well above anything useful for cooking.
Or you mean it'll catch fire? Also not a concern. That is supposed to happen at a temperature well above anything useful for cooking.
The temperature of the blue flame on a stove should be above 1000 Celsius, well above what’s required to oxidise diamonds. They won’t catch fire, but your diamond pan will erode. Once you remove it from the flame, it won’t continue “burning”.
Should be safe on electrical stoves though.
Should be safe on electrical stoves though.
Would that >1000°C reach the surface though?
There are some heady boundary-layer effects and temperature/temp-conductivity gradient physics involved here. For simplicity sake, consider a plastic [1] bag full to the brim with water, held over open flame. Will bag melt (oxidize, erode)?
[1] polyethylene melts around 120-ish °C and ignites around 220-350 °C (sources vary)
There are some heady boundary-layer effects and temperature/temp-conductivity gradient physics involved here. For simplicity sake, consider a plastic [1] bag full to the brim with water, held over open flame. Will bag melt (oxidize, erode)?
[1] polyethylene melts around 120-ish °C and ignites around 220-350 °C (sources vary)
Someone sells a diamond coated pan
https://bluediamondshopping.com/
It's probably fine on the inside?
Why are you using a question mark.
The material would be 'fine', but I'm not sure how safe or effective it would be as I'm not a materials expert. Just considering the risk of the material. (Yeah, the material would be fine, is it safe and beneficial? That part of 'fine' I can't define.)
[deleted]
I think because it will burn your hand?
It’s safe to assume the handle is made from something else.
Just put them on inside only
> But my research group at Stanford University has managed what seemed impossible.
Wait a minute, others have been doing this already: https://www.df.com/
How is this different?
See also: https://youtu.be/ggQKZDZsDec
Wait a minute, others have been doing this already: https://www.df.com/
How is this different?
See also: https://youtu.be/ggQKZDZsDec
What you linked is bonding a diamond substrate to the back of your IC. What's in the post is growing diamond lattice/features directly on your wafer. With the new way, you can get diamond closer to your heat sources, increase contact area, etc.
No idea if it actually matters. Is this a single digit percentage increase in thermal conductivity by messing with a finicky, temperamental process? I don't know. What the paper writers are proposing is under the limit of when transistor structures break down, but not by much.
No idea if it actually matters. Is this a single digit percentage increase in thermal conductivity by messing with a finicky, temperamental process? I don't know. What the paper writers are proposing is under the limit of when transistor structures break down, but not by much.
They mention getting 10's of degrees Celsius improvement. It's very significant.
Nothing new, Applied Diamond has made this stuff for several years and it is incredible. Imagine putting a 15w LED on a typical 20mm star board made of diamond - you do not need a heat sink. Just minor air flow over the package is enough.
A little unlike IEEE to be nearly half a decade out of the loop.
A little unlike IEEE to be nearly half a decade out of the loop.
I think what they have grown diamond on the transistor which then bonds to the substrate through a SIC interlayer.
From what I understand their idea seems to be that since most heating occurs at channels they act like hotspots and therefore it would be much better to drain away heat from them directly.
This is different from creating transistors on a diamond substrate.
From what I understand their idea seems to be that since most heating occurs at channels they act like hotspots and therefore it would be much better to drain away heat from them directly.
This is different from creating transistors on a diamond substrate.
The invention is a fast, low-temperature deposition process, which can then be used directly on a semiconductor device.
Diamond Foundry achieves the same end goal even if the deposition methods and technical processes may differ: https://df.com
They produce the diamond wafers separately and then later bond them, a process that is dramatically more expensive and results in a worse bond.
The new thing here is growing a thin layer of diamond directly on top of a chip.
naturally, graphite has similarly high thermal conductivity along the layer direction (which is basically graphene), and one would think that there should be some way to put such a thin layer of graphite/graphene on top (or inside) the chip to achieve similar results.
Previous discussion: https://news.ycombinator.com/item?id=45654512
This reminded me of this: https://www.innovationcooling.com/products/ic-diamond/?srslt... which seemed to be all the rage in PC building 10 years ago